Preventing Bending Cracks and Processing

Preventing Bending Cracks and Processing Scratches in Stainless Steel

Bending Cracks

• Occurrence: Cracking occurs when the plate is bent.
• Reason: Severe edge burrs cause bending cracks.
• Countermeasure: Reduce edge burrs to prevent bending cracks.

Processing Scratches

• Occurrence: Crack-like defects appear on the surface after forming the steel pipe.
• Reason: Foreign matter on the mold surface causes scratches.
• Countermeasure: Clean the mold surface to prevent scratches.

By addressing edge burrs and keeping molds clean, bending cracks and processing scratches in stainless steel can be minimized.