Là gì Cán nóng?

Hot rolling is done above the metal’s recrystallization temperature.
Recrystallization happens when:

• Heat and time are enough during annealing.

• New, stress-free grains replace deformed ones.

• The metal structure changes fully.

This process improves the metal’s properties.
các recrystallization temperature is the average of the temperatures when:

• New grains first form.

• The structure is fully replaced.

It is influenced by:

• Thành phần hợp kim

• Amount of deformation

• Original grain size

• Annealing temperature

Ưu điểm của Hot-Rolled Stainless Steel

1. Lower Energy Use and Cost

• Less force is needed during hot rolling.

• Energy is saved.

• Costs are reduced.

2. Improved Workability

• Coarse grains from casting are broken.

• Cracks and defects are reduced.

• The structure becomes easier to process.

3. Higher Production Efficiency

• Các phôi lớn và giảm nặng được sử dụng.

• Tốc độ lăn có thể tăng lên.

• Có thể lăn liên tục và tự động.

Nhược điểm của Hot-Rolled Stainless Steel

1. Rủi ro tách lớp

• Bao gồm (như sunfua, oxit) bị san phẳng.

• Sự phân tách có thể xảy ra giữa các lớp.

• Nó làm suy yếu sức mạnh theo hướng độ dày.

• Mối hàn co ngót có thể dẫn đến rách lớp.

2. Căng thẳng dư thừa

• Làm mát không đều gây căng thẳng bên trong.

• Căng thẳng được cân bằng bên trong nhưng không nhìn thấy được.

• Nó có thể gây biến dạng và giảm tuổi thọ mệt mỏi.

• Phần thép dày hơn thường có nhiều ứng suất hơn.

3. Tính chất cơ học kém chính xác hơn

• Độ bền không cao bằng thép gia công nguội.

• Thuộc tính không đồng nhất.

• Độ dẻo nằm giữa thép gia công nguội và thép ủ.

4. Độ dày và kiểm soát bề mặt kém

• Độ dày khó kiểm soát hơn.

• Bề mặt cứng hơn thép cán nguội.

• Độ nhám bề mặt (Ra) là 0.5–1,5 mm cao hơn.

• Sản phẩm cán nóng thường được dùng làm phôi cho cán nguội.