4mm Stainless Plate
- Minimum thickness of hot rolled stainless steel: about 3.0 มม
- Maximum thickness of cold rolled stainless steel: about 3.0 มม (rarely up to 4.0 มม)
A 4mm stainless plate sits at the boundary between hot rolling and cold rolling, but in real industrial production, it is primarily manufactured using hot rolling due to efficiency, ค่าใช้จ่าย, and process limitations.
- คำอธิบาย
ก 4แผ่นเหล็กสแตนเลส มม is typically classified as รีดร้อน (ทรัพยากรบุคคล) rather than cold rolled (CR).
- In industry practice, cold rolled stainless steel is mainly used for thin sheets
- Hot rolled stainless steel ใช้สำหรับ medium to thick plates, including 4mm and above
Minimum Thickness of Hot Rolled Stainless Steel
Hot rolling is suitable for thicker materials, but modern rolling technology can achieve relatively thin gauges.
Typical Hot Rolled Thickness Range
| กระบวนการ | ช่วงความหนา |
|---|---|
| สแตนเลสรีดร้อน | ~3.0 mm – 100 มม.+ |
จุดสำคัญ
- ที่ minimum thickness of hot rolled stainless steel is حوالي 3.0 มม
- Below this thickness, it becomes difficult to control surface quality and dimensional accuracy
บทสรุป:
ก 4mm stainless plate is within the standard hot rolled range, close to the lower limit of hot rolling.
Maximum Thickness of Cold Rolled Stainless Steel
Cold rolling is designed for precision thin materials, but it also has an upper thickness limit.
Typical Cold Rolled Thickness Range
| กระบวนการ | ช่วงความหนา |
|---|---|
| Cold Rolled Stainless Steel | ~0.3 mm – 3.0 มม |
จุดสำคัญ
- ที่ maximum thickness of cold rolled stainless steel is generally around 3.0 มม
- In some advanced mills, it may reach ขึ้นไป 4.0 มม, but this is uncommon and less economical
Why These Limits Exist
Hot Rolling Limitations
- At high temperatures, controlling flatness and surface quality becomes difficult for very thin sheets
- Oxide scale formation affects surface finish
Cold Rolling Limitations
- Requires high rolling force → difficult for thick materials
- Equipment and cost constraints limit thickness
- Increased internal stress in thicker cold rolled sheets
Hot Rolled vs Cold Rolled for 4mm Plate
| คุณสมบัติ | รีดร้อน (4มม) | รีดเย็น (Near Limit) |
|---|---|---|
| Availability | มาตรฐาน | Rare |
| พื้นผิวเสร็จสิ้น | ขรุขระ (ฉบับที่ 1) | เรียบ (2บี) |
| ค่าใช้จ่าย | ต่ำกว่า | สูงกว่า |
| ความเรียบ | ปานกลาง | ดีกว่า |
| แอปพลิเคชัน | โครงสร้าง / ทางอุตสาหกรรม | ความแม่นยำ / ตกแต่ง |
Practical Recommendation
- 4mm stainless plate is almost always hot rolled
- If a smooth surface is required:
- ใช้ ดอง + บด
- Or process from thicker hot rolled plate and finish mechanically