Stainless steel grades 446 e 405 são ferritic stainless steels with specific characteristics suitable for high-temperature and moderate corrosion environments.
1. 446 Aço inoxidável
-
Material Type: Aço inoxidável ferrítico
-
High Temperature Performance: Can withstand impact temperatures up to 1090°C
-
Aplicações Típicas: Steam boiler furnace parts, oil burners, trocadores de calor, kiln linings, glass molds, and fixed soot blowers
Forjamento & Tratamento térmico
-
Forjamento: Preheat uniformly to 815–870°C, then raise to forging temperature range ~1120°C. Perform forging below 900°C. Air cooling and annealing are recommended for forged parts.
-
Recozimento: Conduct annealing at 760–830°C, followed by cooling. Avoid soaking or slow cooling between 370–525°C to prevent embrittlement.
-
Tratamento térmico: Cannot be hardened by standard heat treatment.
Usinagem & Soldagem
-
Usinagem: Can be machined similarly to 442 aço inoxidável; carbide tools are preferred.
-
Soldagem: Standard fusion and resistance welding methods are suitable. Preheat and postheat between 150–315°C. Usar austenitic filler metals como 310 ou 312 stainless steel to maximize weld ductility.
2. 405 Aço inoxidável
-
Material Type: Aço inoxidável ferrítico
-
Resistência à corrosão: Slightly lower than 430 aço inoxidável ferrítico, comparable to 410 aço inoxidável, but with melhor soldabilidade
-
Aplicações Típicas: Similar to low-chromium ferritic steels; suitable for mildly corrosive environments
Forjamento & Tratamento térmico
-
Forjamento: Can be forged in the range 815–1120°C and air-cooled. Aluminum is added to prevent hardening during high-temperature cooling.
-
Recozimento: Heat parts to 780°C, soak, then air-cool. Cannot be hardened by heat treatment.
Usinagem & Soldagem
-
Usinagem: Comparable to other ferritic stainless steels; better mechanical machinability than austenitic stainless steels
-
Soldagem: All normal fusion and resistance methods are suitable. Aluminum addition improves weldability by preventing hardening during weld cooling
Summary Table – 446 contra 405 Propriedades do aço inoxidável
| Recurso | 446 Aço inoxidável | 405 Aço inoxidável |
|---|---|---|
| Stainless Steel Type | Ferrítico | Ferrítico |
| Maximum Service Temp | 1090°C | Moderate temperature |
| Resistência à corrosão | Bom | Moderado, semelhante a 410 |
| Aplicações Típicas | Boilers, burners, trocadores de calor, fornos, glass molds | Mildly corrosive environments |
| Forging Temperature | 815–870°C preheat, 1120°C forging | 815–1120°C |
| Annealing Temperature | 760–830°C | 780°C |
| Tratável termicamente | Não | Não |
| Usinabilidade | Moderado (use carbide tools) | Melhor que os aços austeníticos |
| Soldabilidade | Fusão & soldagem por resistência; pré/pós-aquecimento 150–315°C | Fusão & soldagem por resistência; melhorado pelo alumínio |