GRAD
Grade 409L (UNS S40900, IN 1.4512) is a kind of stabile version of 409, composed with proper chromium, low composition of carbon and nitrogen and adjunction of titanium, all composition appropriate make Grade 409L have some properties, like corrosion resistance, weldability and formability. Due to the lower chromium, Grade 409L was another low cost option for corrosion resistant stainless steel.
It has a good combination of heat resistance and corrosion resistance, can be ideal for non- or lightly corrosive environments or applications. It has excellent oxidation resistance in high temperatures and good welding performance, which can be used for automotive exhaust pipes or oil equipment.
EIGENSCHAFTEN
- Korrosionsbeständigkeit
- Resistance to oxidation
- Excellent resistance to high temperature, exhaust gas and atmospheric corrosion
- Heat treatment
- Zum Schweißen geeignet
- Good flexibility and excellent formability
- Niedrige Kosten
CHEMICAL COMPOSITION AND PHYSICAL PROPERTIES FOR 409L
| Artikel | C% | Und% | Mn% | P% | S% | In% | Cr% | N% | Von% | Anzahl % |
|---|---|---|---|---|---|---|---|---|---|---|
| Min | — | — | — | — | 10.5 | 6(C+N) | ||||
| Max | 0.03 | 1.00 | 1.00 | 0.04 | 0.02 | 0.5 | 11.7 | 0.03 | 0.5 | 0.17 |
| Artikel | Zugversuch | Härtetest | Biegetest | ||||
|---|---|---|---|---|---|---|---|
| 0.2%Y.S.. | 1%Y.S.. | T.S. | ER (%) | HRW | HV | 180∘ | |
| Min | 170 | — | 380 | 20 | — | — | 0.5T |
| Max | N/mm2 | — | N/mm2 | — | 88 | — | |
ANWENDUNG
- Abgassysteme für Kraftfahrzeuge (manifolds, exhaust pipes, converters, front and tail pipes, converters, mufflers and other components)
- Wärmetauscher
- Catalytic converter systems
- Culverts
- Home heating systems
- Automotive thermostats
- Fuel filters
- Farm equipment components
- Electrical transformer cases
SPEZIFIKATIONEN
- ASTM A240M – Chrom und Chrom – Nickel-Edelstahlplatte, Bleche und Bänder für Druckbehälter und für allgemeine Anwendungen.
- ASTM 480M – Allgemeine Anforderungen für flachgewalzte rostfreie und hitzebeständige Stahlplatten, Blatt und Streifen
- IN 10088-2 (1.4512) – Edelstahl Technische Lieferbedingungen für Blech, Bleche und Bänder aus korrosionsbeständigem Stahl für allgemeine Zwecke
ROHSTOFFVERARBEITUNG & VERFÜGBARE GRÖSSEN
| 2D | Eine Uniform, mattes silbergraues Finish, das durch Kaltwalzen mit anschließendem Glühen und Entzundern entsteht. | |||||
|---|---|---|---|---|---|---|
| Reichweite | 914 (3′) | 1000 | 1219 (4′) | 1250 | 1500 | 1524 (5′) |
| 0.3mm ~ 3,0 mm | ◇ | ◆ | ◆ | ◆ | ◆ | ◆ |
| 30GA ~ 11GA | ◇ | ◆ | ◆ | ◆ | ◆ | ◆ |
| 0.012″ ~ 0,1196″ | ◇ | ◆ | ◆ | ◆ | ◆ | ◆ |
| 2B (Mühlenfinish) |
Ein helles, Kaltgewalztes Finish, das auf die gleiche Weise wie das 2D-Finish resultiert, mit der Ausnahme, dass das geglühte und entzunderte Blech einen abschließenden leichten Walzdurchlauf durch polierte Walzen erhielt. Dies ist die allgemein verwendbare kaltgewalzte Oberfläche, oder als Vorstufe zum Polieren. | |||||
| Reichweite | 914 (3′) | 1000 | 1219 (4′) | 1250 | 1500 | 1524 (5′) |
| 0.3mm ~ 3,0 mm | ◇ | ◆ | ◆ | ◆ | ◆ | ◆ |
| 30GA ~ 11GA | ◇ | ◆ | ◆ | ◆ | ◆ | ◆ |
| 0.012″ ~ 0,1196″ | ◇ | ◆ | ◆ | ◆ | ◆ | ◆ |